Colossae Beige More Fossil is best choice to emphasize naturalness in your residential and commercial implementations with its fossil texture and mixed surface.
Colossae Beige More Fossil is best choice to emphasize naturalness in your residential and commercial implementations with its fossil texture and mixed surface.
Test Results
| Physical Parameters | Unit | Range | Avarage Value |
| Strach hardness according to Mohs scale | Mohs | - | 3 |
| Real density | kg/m3 | - | 2.718 |
| Schmidt hardness rebound number | - | 32-40 | 37 |
| Dry unit weight | gr/cm3 | 2.39-2.50 | 2.45 |
| Saturated unit weight | (%) | 2.47-2.55 | 2.51 |
| Water absorption at atmospheric pressure | (%) | 2.01-3.59 | 2.67 |
| Absorption by volume | (%) | 5.06-8.69 | 6.58 |
| Apparent porosity | (%) | 5.06-8.69 | 6.58 |
| Total porosity | - | 7.49-10.92 | 9.03 |
| Compasity | (%) | 81.63-85.68 | 83.39 |
| Water absorption coefficient by capillarity | g/m2.s0.5 | 7.62-13.83 | 10.46 |
| Capillarity water absorption | (%) | 1.84-3.44 | 2.56 |
| Vertical abrasion resistance | mm | 20-26 | 24 |
| Reaction to fire | Class | - | A1 |
| Mechanical Parameters | Unit | Values | Avarage Value |
| Uniaxial compressive strength (dry) | MPa | 57.93-84.06 | 69.56 |
| Uniaxial compressive strength (saturated) | MPa | 43.52-61.32 | 51.19 |
| Uniaxial compressive strength after freezing | MPa | - | - |
| Flexural strength under concentrated load | MPa | 9.06-14.17 | 11.67 |
| Flexural strength under constant moment | Mpa | 9.97-15.40 | 12.33 |
| Slip Resistance (Dry condition, unpolished surface) | - | 52-57 | 55 |
| Slip Resistance (Dry condition, polished surface) | - | 58-62 | 60 |