Nyks Cross Cut‘s structure which is formed with unique beige tonnes turns into a perfect product by integration of soft colour transition. Nyks Cross Cut is the first of the options to create classy spaces.
Nyks Cross Cut‘s structure which is formed with unique beige tonnes turns into a perfect product by integration of soft colour transition. Nyks Cross Cut is the first of the options to create classy spaces.
Test Results
| Physical Parameters | Unit | Range | Avarage Value |
| Strach hardness according to Mohs scale | Mohs | - | 3 |
| Real density | kg/m3 | - | 2.695 |
| Dry unit weight | gr/cm3 | 2.14-2.31 | 2.28 |
| Saturated unit weight | gr/cm3 | 2.37-2.41 | 2.39 |
| Water absorption at atmospheric pressure | (%) | 4.01-4.89 | 4.52 |
| Absorption by volume | (%) | 9.36-11.12 | 10.41 |
| Apparent porosity | (%) | 9.36-11.12 | 10.41 |
| Total porosity | (%) | 13.43-15.58 | 14.54 |
| Compasity | (%) | 79.25-85.64 | 83.95 |
| Water absorption coefficient by capillarity | g/m2.s0.5 | - | - |
| Capillarity water absorption | (%) | 3.31-4.16 | 3.81 |
| Vertical abrasion resistance | mm | 17.95-27.87 | 23.57 |
| Reaction to fire | Class | - | A1 |
| Mechanical Parameters | Unit | Values | Avarage Value |
| Uniaxial compressive strength (dry) | MPa | 36.52-69.09 | 53.98 |
| Uniaxial compressive strength (saturated) | MPa | 30.76-42.46 | 36.98 |
| Uniaxial compressive strength after freezing | MPa | 31.11-38.26 | 32.54 |
| Flexural strength under concentrated load | MPa | 6.73-10.79 | 9.5 |
| Flexural strength under constant moment | Mpa | 6.74-9.78 | 8.12 |
| Slip Resistance (Dry condition, polished surface, ps) | - | 68-74 | 68 |
| Slip Resistance (Dry condition, polished surface vs) | - | 60-64 | 62 |
| Slip Resistance (Dry condition, honed surface, ps) | - | 62-66 | 64 |
| Slip Resistance (Dry condition, honed surface vs) | - | 64-68 | 65 |
| ps: parallel skid, vs: vertical skid |